S-320 Zirconia alumina composite beads

 S-320 Zirconia alumina composite beads    size: 0.6-6mm

 composition:

 ZrO₂>25%, Al₂O₃>25%，SiO₂ >45%

 Specific density:

 3.2g/cm³

 Bulk density:

 2.0g/cm³

 Mohs hardness

 8

 Whiteness:

 >92

 Water absorption:

 <0.02%

Application: 1, non-metallic minerals such as: calcium carbonate, kaolin, magnetic materials and other minerals

     2, paint industry, such as: paint, ink, paint and so on.

     3,recommended machine, 80L-3600L vertical sand mill.The density is higher than SR-270, the internal structure is fine, fine grain, good wear resistance. For high-speed machines with high solid content, abrasive and high concentration slurry. And the product surface is smooth, wear and tear on the equipment inner tube is quite small.

Packing: 25kg 500kg 1000kg